Piezoceramic Components and Actuators
Piezoelectric Elements in Different Shapes
Piezo ceramic solutions to all important high-tech markets: Industrial automation, semiconductor technology, medical technology, mechanical and precision engineering, aviation and aerospace, automotive industry and telecommunications.
Piezoceramic components, such as plates, disks or rings, convert mechanical signals, such as force, pressure, strain or acceleration, into electrical voltage, or, vice versa, an electrical voltage into mechanical motion or oscillations. The typical resonant frequencies are between 200 kHz and 10 MHz. The shapes and dimensions of the piezo components can be selected within the limits determined by the tools, although the dimensions depend on each other. The minimum dimensions are determined by physical and technological limits. The thickness or wall thickness, for example, is limited by the mechanical strength of the ceramic during machining. In the polarization direction, the dimension is at most 30 mm.
Piezoceramic Materials
Piezo Materials Based on Lead Zirconate Titanate (PZT)
PI Ceramic provides a wide selection of piezoelectric ceramic materials based on modified lead zirconate titanate (PZT) and barium titanate. The designations of "soft" and "hard" piezo ceramics refer to the mobility of the dipoles or domains and hence also to the polarization and depolarization behavior. For actuator applications, ferroelectrically soft piezoceramics with low polarity reversal field strengths are used. Ferroelectrically hard PZT materials are primarily used in high-power acoustic applications. In addition, PI Ceramic offers lead-free piezo ceramics, currently used especially as ultrasonic transducers, and a crystalline actuator material.
For application-specific properties, actuators and transducers can be manufactured from special materials, although the technical implementation has to be checked individually.
The material properties are classified according to the EN 50324 European Standard.
Soft Piezoelectric Materials
Soft Piezoelectric Materials
Ideal for Piezo Actuators and Sensors
Ferroelectrically soft piezo ceramic materials can be polarized fairly easily even at relatively low field strengths. This is due to the comparably high domain mobility typical for them. The advantages of soft PZT materials are their large piezoelectric charge coefficient, moderate permittivities and high coupling factors.
Applications
Important fields of application for soft piezo ceramics are: Actuators for micropositioning and nanopositioning, sensors, such as conventional vibration detectors, ultrasonic transmitters and receivers, e.g., for flow or level measurement, object identification or monitoring, as well as for electro-acoustic applications as sound transducers and microphones, and also as sound pickups on musical instruments.
| PIC151 | Standard material for actuators of the PICA Stack/Thru and Piezo Tubes series |
|---|---|
| Material | Modified lead zirconate titanate |
| Characteristics | High permittivity, large coupling factor, high piezoelectric charge coefficient, relatively high Curie temperature |
| Suitable for | Actuators, low-power ultrasonic transducers, low-frequency sound transducers |
| Classification in accordance with EN 50324-1 | 600 |
| MIL-Standard DOD-STD-1376A | II |
| PIC255 | Standard material for PICA Power, DuraAct, PICA Shear, and Piezo Tubes series |
|---|---|
| Material | Modified lead zirconate titanate |
| Characteristics | Very high Curie temperature, moderate permittivity, high coupling factor, high charge coefficient, low mechanical quality factor, low temperature coefficient, relatively high polarity reversal field strength (>1 kV/mm) |
| Suitable for | Actuator applications for dynamic operating conditions and high ambient temperatures, low-power ultrasonic transducers, nonresonant broadband systems, force and acoustic pickup sensors |
| Classification in accordance with EN 50324-1 | 200 |
| MIL-Standard DOD-STD-1376A | II |
| PIC155 | |
|---|---|
| Material | Modified lead zirconate titanate |
| Characteristics | Very high Curie temperature, moderate permittivity, low mechanical quality factor, low temperature coefficient, high sensitivity (g coefficients) |
| Suitable for | Applications which require a high g coefficient (piezoelectric voltage coefficient), e.g., for microphones and vibration pickups with preamplifier, vibration measurements at low frequencies |
| Classification in accordance with EN 50324-1 | 200 |
| MIL-Standard DOD-STD-1376A | II |
| PIC153 | Material for special actuators of the PICA Stack/Thru series and for glued bending actuators |
|---|---|
| Material | Modified lead zirconate titanate |
| Characteristics | Extremely high permittivity and coupling factors, high charge coefficient, Curie temperature around 185 °C |
| Suitable for | Hydrophones, transducers in medical diagnostics and PZT translators |
| Classification in accordance with EN 50324-1 | 600 |
| MIL-Standard DOD-STD-1376A | VI |
| PIC152 | |
|---|---|
| Material | Modified lead zirconate titanate |
| Characteristics | Permittivity with extremely low temperature coefficient |
| Suitable for | Force and acceleration transducers |
| Classification in accordance with EN 50324-1 | 200 |
| MIL-Standard DOD-STD-1376A | II |
Hard Piezoelectric Materials
High-Performance Material for Ultrasonic Transducers
Ferroelectrically hard PZT materials can be subjected to high electrical and mechanical stresses. Their properties hardly change under these conditions.
The advantages of these materials are their moderate permittivity, large piezoelectric coupling factors, high mechanical qualities, and very good stability under high mechanical loads and operating field strengths. Low dielectric losses facilitate their continuous use in resonance mode with only low intrinsic heating of the component.
Applications
Especially high-power acoustic applications benefit from the properties of hard piezo materials. Examples of their fields of application include ultrasonic cleaning (typically in the kHz frequency range), the machining of materials (ultrasonic welding, bonding, drilling, etc.), ultrasonic processors (e.g., to disperse liquid media), the medical sector (ultrasonic tartar removal, surgical instruments, etc.) and sonar technology.
Material Properties and Classification
| PIC181 | |
|---|---|
| Material | Modified lead zirconate titanate |
| Characteristics | Extremely high mechanical quality factor, good temperature, and time stability of its dielectric and elasticity constants |
| Suitable for | High-power acoustic applications, resonance-mode ultrasonic applications |
| Classification in accordance with EN 50324-1 | 100 |
| MIL-Standard DOD-STD-1376A | I |
| PIC184 | |
|---|---|
| Material | Modified lead zirconate titanate |
| Characteristics | Large electromechanical coupling factor, moderately high quality factor, excellent mechanical and electrical stability |
| Suitable for | High-power ultrasound applications, hydroacoustics, sonar technology |
| Classification in accordance with EN 50324-1 | 100 |
| MIL-Standard DOD-STD-1376A | I |
| PIC144 | |
|---|---|
| Material | Modified lead zirconate titanate |
| Characteristics | Large electromechanical coupling factor, high quality factor, excellent mechanical and electrical stability, high compressive resistance |
| Suitable for | High-power ultrasound applications, hydroacoustics, sonar technology |
| Classification in accordance with EN 50324-1 | 100 |
| MIL-Standard DOD-STD-1376A | I |
| PIC241 | |
|---|---|
| Material | Modified lead zirconate titanate |
| Characteristics | High mechanical quality factor, higher permittivity than PIC181 |
| Suitable for | High-power acoustic applications, piezomotor drives |
| Classification in accordance with EN 50324-1 | 100 |
| MIL-Standard DOD-STD-1376A | I |
| PIC300 | |
|---|---|
| Material | Modified lead zirconate titanate |
| Characteristics | Very high Curie temperature |
| Suitable for | Use at temperatures up to 250 °C (briefly up to 300 °C) |
| Classification in accordance with EN 50324-1 | 100 |
| MIL-Standard DOD-STD-1376A | I |
Lead-Free Piezoelectric Materials
PI Ceramic offers lead-free piezoceramics from laboratory production. The materials are based on bismuth sodium titanate (BNT) and show very similar properties to barium titanate materials. The materials are suitable for ultrasonic transducers in the MHz range as well as for sonar and hydrophone applications.
Material Data
Material Data
Thermal Properties Using PZT Ceramic PIC255 as Example
Thermal Properties Using PZT Ceramic PIC255 as Example
The thermal strain exhibits different behavior in the polarization direction and perpendicularly to it.
Nonpolarized piezoceramic elements are isotropic. The coefficient of expansion is approximately linear at a temperature coefficient of approx 2 × 10-6 / K.
The preferred orientation of the domains in a polarized PZT body leads to anisotropy, which is the cause of the varying thermal expansion behavior.
The effect of successive temperature changes must be taken into account in the application. Large changes in the curve can occur particularly in the first temperature cycle.
Depending on the material, it is possible that the curves deviate strongly from those illustrated.
Downloads
Piezoelectric Actuators
Components, Technologies, Operation
PI Ceramic RoHS Statement
Restriction of the use of certain hazardous substances in electrical and electronic equipment – RoHS 2011 / 65 / EU
Material Data
PI Ceramic REACH Regulation
Customer Information in Accordance with Article 33 (1) of the REACH Regulation
PI Piezoelectric Ceramic Products
Fundamentals, Characteristics and Applications